ZTA Ceramic Heads/Inserts
The golden standard choice for the bearing in primary THA.
⊚
Exceptional wear resistance with minimal wear.
Superior biocompatibility.
High hardness and high fracture toughness.
- Vickers Hardness 20.5GPa
- Biaxial Bending Strength 1179MPa
- Four-Point Bending Strength 1334MPa
- Fracture Toughness 6.08MPa.m1/2
TZP Ceramic Heads
To experience the less wear of CoXP THA.
⊚
Using for hard-on-soft bearing of mainstream global applications.
Exceptional wear resistance with minimal wear.
Extremely high hardness and scratch resistance.
- Vickers Hardness 12.5GPa
- Four-Point Bending Strength 1800MPa
- Fracture Toughness 10.5MPa.m1/2
- Hydrothermal Aging 4.1%
Ceramic Heads with Sleeve
Ceramic heads with metal sleeve enhance the safety of revision THA.
⊚
A safe and reliable solution in revision THA.
28mm XL head used in primary THA.
A bearing upgrade solution for metal ball head in revision YHA.
- Vickers Hardness 20.5GPa
- Biaxial Bending Strength 1179MPa
- Four-Point Bending Strength 1334MPa
- Fracture Toughness 6.08MPa.m1/2
Ceramic HRA
Material upgrade solution for traditional MoM.
⊚
For active patients, it reduces the implant components number, while increasing the range of motion and decerasing the dislocation.
Minimally invasive procedures reduce the bone resection, enabling patients to recover rapidly.
- Vickers Hardness 20.5GPa
- Biaxial Bending Strength 1179MPa
- Four-Point Bending Strength 1334MPa
- Fracture Toughness 6.08MPa.m1/2
Dual Mobility THA with Ceramic Inerts
Dual Mobility THA with ceramic inerts represents the superior solution.
⊚
Whether for primary or revision THA, ceramic DM THA can significantly reduce the dislocation.
The use of ceramic insert can completely alleviated surgeons' concerns for fretting/corrosion between the metal insert and cup wall.
- Vickers Hardness 20.5GPa
- Biaxial Bending Strength 1179MPa
- Four-Point Bending Strength 1334MPa
- Fracture Toughness 6.08MPa.m1/2
Ceramic Shoulders
A novel solution for patients with metal allergies.
⊚
The material presents no issues with metal ion release or metal allergies, making it a new choice for shoulder replacement.
The product is available in multiple models.
- Vickers Hardness 20.5GPa
- Biaxial Bending Strength 1179MPa
- Four-Point Bending Strength 1334MPa
- Fracture Toughness 6.08MPa.m1/2
- 维氏硬度 20.5GPa
- 双轴抗弯强度 1179MPa
- 四点抗弯强度 1334MPa
- 断裂韧性 6.08MPa.m1/2
Ceramic TKA
The robust characteristics enable the production of specialised femoral condyles.
⊚
The material properties of high strength and high fracture toughness have made the advent of non-standard femoral condyle components possible.
High wear resistance, low wear.
- Vickers Hardness 12.5GPa
- Four-Point Bending Strength 1800MPa
- Fracture Toughness 10.5MPa.m1/2
- Hydrothermal Aging 4.1%
Ceramic UKA
The robust characteristics enable the production of specialised UKA.
⊚
The material properties of high strength and high fracture toughness have made the advent of non-standard unicondylar components possible.
High wear resistance, low wear.
- Vickers Hardness 12.5GPa
- Four-Point Bending Strength 1800MPa
- Fracture Toughness 10.5MPa.m1/2
- Hydrothermal Aging 4.1%
- 标签5
- 标签6
Two-Piece Ceramic Dental Implants
Significantly reduce the incidence of peri-implantitis.
⊚
It significantly enhances the aesthetic outcome of the implant.
The ceramic surface reduces biofilm formation, substantially lowering the incidence of complications such as peri-implantitis.
Two times of procedure mkae more reliable postoperative results.
- Vickers Hardness 12.5GPa
- Four-Point Bending Strength 1800MPa
- Fracture Toughness 10.5MPa.m1/2
- Hydrothermal Aging 4.1%
One-Piece Ceramic Dental Implants
An affordable and high-quality implant option for rapid recovery.
⊚
It significantly enhances the aesthetic outcome of the implant.
The ceramic surface reduces biofilm formation, substantially lowering the incidence of complications such as peri-implantitis.
A single procedure minimises disruption to the patient, facilitating rapid recovery.
- Vickers Hardness 12.5GPa
- Four-Point Bending Strength 1800MPa
- Fracture Toughness 10.5MPa.m1/2
- Hydrothermal Aging 4.1%
- 标签5
Ceramic Veterinary Heads
The ceramic heads provides an ideal solution for animal hip dislocation.
⊚
A comprehensive range of models to fully address the anatomical requirements of cats, small dogs, and large dogs.
Excellent biocompatibility.
- Vickers Hardness 20.5GPa
- Biaxial Bending Strength 1179MPa
- Four-Point Bending Strength 1334MPa
- Fracture Toughness 6.08MPa.m1/2